Schlüsseleigenschaften F – AW Key Characteristics F-AW
|
Schlüsseleigenschaften F – AW Key Characteristics F-AW | |||
|
Zusammensetzung/ Compositiom |
Mn • Zn • Fe | ||
|
Formen/Shapes |
Toroid | ||
|
Größe/Sizes |
3.0mm bis 140 mm | ||
|
Beschichtungscode |
Parylene-Beschichtung Parylene Coating | ||
|
Beschichtungsfarbe/ Coating Color |
Grau | ||
|
|
M |
Permeability: |
15.000 µi ±30% |
|
|
W |
|
10.000 µi ±30% |
|
J |
5.000 µi ±20% | ||
|
T |
3000 µi ±25% | ||
|
F |
3000 µi ±20% | ||
|
P |
2.500 µi ±25% | ||
|
R |
2.300 µi ±25% | ||
|
L |
900 µi ±25% | ||
|
C |
900 µi ±25% | ||
Typische Anwendungen für hochpermeable Ferrit-Toroide, 5.000μ J-Material, 10.000μW-Material und 15.000μM-Material umfassen Gleichtaktdrosseln, EMI-Filter, Breitbandtransformatoren, Impulstransformatoren und Stromwandler.
Spezielle Größen von Ferrit-Toroiden sind in 5.000 J Material für Erdschlussunterbrecheranwendungen (GFCI) verfügbar. 900μ L Material, 2.300μ R Material, 2.500μ P Material und 3.000μ F Materialtoiden sind eine ausgezeichnete Wahl für Hochfrequenztransformatoren.
Ferrit-Toroide bieten eine hohe magnetische Effizienz, da kein Luftspalt vorhanden ist und die Querschnittsfläche gleichmäßig ist. Ferrite sind in vielen Größen (Außendurchmesser von 2 mm bis 140 mm) und Materialien (Permeabilitäten von 800μ bis 15.000μ) erhältlich.
Zusammenfassung der Ferritmaterialien für alle magnetischen Ferritmaterialien mit hoher Permeabilität und hoher Permeabilität.
Induktoren und Leistungstransformatoren - F (3.000μ), T (3.000μ)
EMI / RFI-Filter und Breitbandtransformatoren - J (5.000μ), W (10.000μ), M (15.000μ)
Power Design mit Ferritkernen für Induktivitäten und Transformatoren.
Typical applications for high permeability ferrite toroids, 5,000µ J material, 10,000µ W material, and 15,000µ M material include common mode chokes, EMI filters, broadband transformers, pulse transformers and current transformers. Special sizes of ferrite toroids are available in 5,000 J material for Ground Fault Interrupter (GFCI) applications. 900µ L material, 2,300µ R material, 2,500µ P material, and 3,000µ F material toroids are excellent choices for high frequency transformers.
|
|
INDUCTORS & POWER TRANSFORMER |
EMI/RFI FILTERS & BROADBAND TRANSFORMERS | |||||||||
|
Material |
|
|
L |
R |
P |
F |
T |
J |
W | ||
|
Inital Permeability |
µi |
|
900 ±25% |
2.300 ±25% |
2.500 ±25% |
3.000 ±25% |
3.000 ±25% |
5.000 ±20% |
10.000 ±30% | ||
|
Maxium Usable Frequency
|
f |
MHz |
±3 |
≤1.8 |
≤1.8 |
≤1.5 |
≤1.5 |
≤0.7 |
≤0.5 | ||
|
Relative Loss Factor X 10-6 25°C |
|
Tanδ/ µiac |
|
≤15 (100kHz) |
˂7 (10 kHz) | ||||||
|
Curie Temperature |
Tc |
°C |
˃300 |
˃210 |
˃210 |
˃210 |
˃210 |
˃220 |
˃145 | ||
|
Flux Density@1.194 A/m /15oe) 25°C |
Bm 10 kHz |
G mT |
4.200 420 |
4.700 470 |
4.700 470 |
4.700 470 |
5.300 530 |
4.300 430 |
3.900 390 | ||
|
Remanence 25°C |
Br |
G mT |
1.500 150 |
1.600 160 |
1.600 160 |
1.500 150 |
1.500 150 |
1.000 100 |
800 80 | ||
|
Power Loss (PL) Sine Wave, in mW/cm³ (Typical) |
25 kHz |
@25°C |
|
90 |
180 |
60 |
80 |
| |||
|
200 mT |
@60°C |
65 |
110 |
55 |
75 | ||||||
|
(2.000 G) |
@100°C |
60 |
65 |
90 |
70 | ||||||
|
|
|
@120°C |
65 |
110 |
125 |
75 | |||||
|
100 kHz |
@25°C |
87 |
70 |
70 |
65 | ||||||
|
100 mT |
@60°C |
64 |
50 |
65 |
57 | ||||||
|
(1.000G) |
@100°C |
58 |
65 |
110 |
55 | ||||||
|
@120°C |
64 |
45 |
150 |
58 | |||||||
|
500 kHz |
@25°C |
290 |
| ||||||||
|
50 mT |
@60°C |
150 | |||||||||
|
(500 G) |
@100°C |
115 |
175 |
300 |
|
150 | |||||
|
@120°C |
130 |
| |||||||||
|
Resistivity |
P |
Ω-m |
10 |
5 |
5 |
5 |
5 |
0.5 |
0.1 | ||
|
Density |
δ |
g/cm³ |
4.8 |
4.8 |
4.8 |
4.8 |
4.8 |
4.8 |
4.9 | ||