T184-6

MATERIAL 6 (Permeabilität 8)

Ein "SF"-gepulvertes Eisenmaterial, das dem Material "2" sehr ähnelt, aber verbesserte Güte für höhere Frequenzen bis 50 MHz aufweist.

Kern

Farbe

Außen

Innen

Höhe

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

Product Group

T184-6

Gelb

46.74

24.13

18.03

µ 8

195

±5%

2-50 MHz

110

gramm

A_Lvalue (nominal)

19.5 nH/ N²

μi (reference)

µ 8

Density gm/cm³

5.0

Test Winding

N=100, #24 AWG

Frequency

10 kHz

Voltage on Agilent 4284A

0.83 V

Coating Type

Yellow/Clear Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

11.2 cm

1.88 cm²

21 cm³

4.34 cm²

80.9 cm²

7.32 cm

Core Loss

Q Test Winding

#N/A

Q Frequenzy

#N/A

Q min on HP4342A

#N/A

where Bpk expressed in gauss, f expressed in hertz, and:

a=4.00E+09, b=3.00E+08, c=2.70E+06, d=8.90E-16

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

200 Oe

98,1%

97.4%

where H expressed in oersteds, and:

a=1.00E-02, b=4.87E-08, c=1.57, d=0.00

Wire Size

AWG

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

111

139

174

RDC(Ω)

2.6 m

5.3 m

10.7 m

21.8 m

43.3 m

87.3 m

173.0 m

344.8 m

683.9 m

1.4

2.7

Full Winding

Turns

130

202

312

483

747

1,157

1,790

RDC(Ω)

3.5 m

8.4 m

20.6 m

50.9 m

125.2 m

309.4 m

760.0 m

1.9

4.6

11.3

27.9

T184-11

Material 11 (Permeabilität 20)

Ein "C"-gepulvertes Carbonyleisenmaterial, das dem Material '13' sehr ähnelt, aber einen höheren Volumenwiderstand und eine größere Stabilität aufweist.

Kern

Farbe

Außen

Innen

Höhe

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

Product Group

T184-11

Blau

46.74

24.13

18.03

µ 20

500

±10%

0.5-5

130

gramm

A_Lvalue (nominal)

50 nH/ N²

μi (reference)

µ 20

Density gm/cm³

6.4

Test Winding

N=100, #24 AWG

Frequency

10 kHz

Voltage on Agilent 4284A

0.83 V

Coating Type

Blue/Clear Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

11.2 cm

1.88 cm²

21 cm³

4.34 cm²

80.9 cm²

7.32 cm

Core Loss

Bpk

140 G

Frequenzy

100 kHz

Core Loss (nominal)

31 mW/cm³

Core Loss (maximum)

36 mW/cm³

where Bpk expressed in gauss, f expressed in hertz, and:

a=1.90E+09, b=2.00E+08, c=9.00E+05, d=4.30E-15

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

200 Oe

82.2%

78.0%

where H expressed in oersteds, and:

a=1.00E-02, b=1.14E-06, c=1.43, d=0.00

Wire Size

AWG

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

111

139

174

RDC(Ω)

2.6 m

5.3 m

10.7 m

21.8 m

43.3 m

87.3 m

173.0 m

344.8 m

683.9 m

1.4

2.7

Full Winding

Turns

130

202

312

483

747

1,157

1,790

RDC(Ω)

3.5 m

8.4 m

20.6 m

50.9 m

125.2 m

309.4 m

760.0 m

1.9

4.6

11.3

27.9

T184-13

MATERIAL 13 (Permeabilität 35)

Ein "HP"-gepulvertes Carbonyleisenmaterial mit ausgezeichneter Stabilität und hoher Güte für niedrige Frequenzen um 50 kHz.

Kern

Farbe

Außen

Innen

Höhe

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

Product Group

T184-13

Grau

46.74

24.13

18.03

µ 35

720

±10%

0.05-0.5

140

gramm

A_Lvalue (nominal)

72 nH/ N²

μi (reference)

µ 35

Density gm/cm³

6.5

Test Winding

N=100, #24 AWG

Frequency

10 kHz

Voltage on Agilent 4284A

0.83 V

Coating Type

Gray/Clear Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

11.2 cm

1.88 cm²

21 cm³

4.34 cm²

80.9 cm²

7.32 cm

Core Loss

Bpk

140 G

Frequenzy

100 kHz

Core Loss (nominal)

31 mW/cm³

Core Loss (maximum)

36 mW/cm³

where Bpk expressed in gauss, f expressed in hertz, and:

a=1.90E+09, b=2.00E+08, c=9.00E+05, d=4.30E-15

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

200 Oe

60.1%

53.7%

where H expressed in oersteds, and:

a=1.00E-02, b=3.49E-06, c=1.43, d=0.00

Wire Size

AWG

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

111

139

174

RDC(Ω)

2.6 m

5.3 m

10.7 m

21.8 m

43.3 m

87.3 m

173.0 m

344.8 m

683.9 m

1.4

2.7

Full Winding

Turns

130

202

312

483

747

1,157

1,790

RDC(Ω)

3.5 m

8.4 m

20.6 m

50.9 m

125.2 m

309.4 m

760.0 m

1.9

4.6

11.3

27.9

T184-17

MATERIAL 17 - Permeabilität 4

Ein synthetisches Oxidmaterial, das eine mittlere Güte und Stabilität oberhalb von 100 MHz besitzt.

Material 17 Ähnelt sehr dem Material 12, hat aber einen stark verringerten Temperaturgang. Die Güte, die bei Benutzung dieses Materials erreicht werden kann, liegt um etwa 10% unter der von Material "12". Dies sollte aber hingenommen werden, wenn geringere Temperaturgang von vorrangiger Bedeutung ist.

10 & -17 Materialien: Diese Materialien sind Carbonyl Irons mit der höchsten Frequenz. Sie bieten hohe Q-Werte bis zu 150 MHz und sind ein beliebtes Material für Kabelfernsehanwendungen. Sie werden moderate Bandtransformatoren produzieren, die 400 bis 700 MHz abdecken.

Kern

Farbe

Außen

Innen

Höhe

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

Product Group

T184-17

Blau/

Gelb

46.74

24.13

18.03

µ 4

±5%

20-200

100

gramm

A_Lvalue (nominal)

8.7 nH/ N²

μi (reference)

µ 4

Density gm/cm³

4.8

Test Winding

N=100, #24 AWG

Frequency

1 MHz

Voltage on Agilent 4284A

1.0 V

Coating Type

Blue/Yellow Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

11.2 cm

1.88 cm²

21 cm³

4.34 cm²

80.9 cm²

7.32 cm

Core Loss

Q test winding

N=6, #18 AWG

Q Frequenzy

25 MHz

Q min on HP4342A

256

where Bpk expressed in gauss, f expressed in hertz, and:

a=4.00E+09, b=3.00E+08, c=2.70E+06, d=4.40E-16

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

200 Oe

99.5%

99.4%

where H expressed in oersteds, and:

a=1.00E-02, b=1.34E-08, c=1.55, d=0.00

Wire Size

AWG

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

111

139

174

RDC(Ω)

2.6 m

5.3 m

10.7 m

21.8 m

43.3 m

87.3 m

173.0 m

344.8 m

683.9 m

1.4

2.7

Full Winding

Turns

130

202

312

483

747

1,157

1,790

RDC(Ω)

3.5 m

8.4 m

20.6 m

50.9 m

125.2 m

309.4 m

760.0 m

1.9

4.6

11.3

27.9

10 & ‐17 Materials: These materials are the highest frequency carbonyl irons. They will provide high Q up to 150 MHz and are a popular material for cable television applications. They will produce moderate band transformers covering 400 to 700 MHz.

T184-18

MATERIAL 18 (Permeabilität 55)

Dieses Material hat einen geringen Kernverlust wie das Material -8 mit höherer Permeabilität. Gute DC-Sättigungseigenschaften.

Für Leistungsanwendung 50/60Hz - bis 500 kHz

Preis-und Lieferzeit auf Anfrage

Kern

Farbe

Außen

Innen

Höhe

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

Product Group

T184-18

Grün/

Rot

46.74

24.13

18.03

µ 55

1160

±10%

DC-Drosseln-Leistungsdrossel

140

gramm

A_Lvalue (nominal)

116 nH/ N²

μi (reference)

µ 55

Density gm/cm³

6.6

Test Winding

N=100, #24 AWG

Frequency

10 kHz

Voltage on Agilent 4284A

0.83 V

Coating Type

Green/Red Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

11.2 cm

1.88 cm²

21 cm³

4.34 cm²

80.9 cm²

7.32 cm

Core Loss

Bpk

140 G

Frequenzy

100 kHz

Core Loss (nominal)

46 mW/cm³

Core Loss (maximum)

53 mW/cm³

where Bpk expressed in gauss, f expressed in hertz, and:

a=8.00E+08, b=1.70E+08, c=9.00E+05, d=3.10E-14

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

100 Oe

51.4%

43.9%

where H expressed in oersteds, and:

a=1.00E-02, b=4.72E-06, c=1.65, d=0.00

Wire Size

AWG

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

111

139

174

RDC(Ω)

2.6 m

5.3 m

10.7 m

21.8 m

43.3 m

87.3 m

173.0 m

344.8 m

683.9 m

1.4

2.7

Full Winding

Turns

130

202

312

483

747

1,157

1,790

RDC(Ω)

3.5 m

8.4 m

20.6 m

50.9 m

125.2 m

309.4 m

760.0 m

1.9

4.6

11.3

27.9

T184-26

MATERIAL 26 (Permeabilität 70)

-26- & 36 Material: Ein sehr populäres Material, es ist ein kostengünstiges Allzweckmaterial, das in einer Vielzahl von Stromumwandlungs- und Netzfilteranwendungen nützlich ist.

Ein wasserstoffreduziertes Eisenmaterial, das Material '41' sehr ähnelt, aber einen erweiterten Frequenzbereich bietet.

50/60Hz - bis 500 kHz für Leistungsan

Bevorzugte Anwendungsbereiche:
Licht-Dimmer-Drosseln 50/60 Hz,

EMI-Netz Drosseln

DC-Drosseln <50 kHz

Leistungsfaktor-Korrektur Drosseln <50 kHz.

Kern

Farbe

Außen

Innen

Höhe

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

Product Group

T184-26

Gelb/Weiß

46.74

24.13

18.03

µ 70

1690

±10%

DC—1 MHz

150

gramm

A_Lvalue (nominal)

169 nH/ N²

μi (reference)

µ 70

Density gm/cm³

7.0

Test Winding

N=100, #24 AWG

Frequency

10 kHz

Voltage on Agilent 4284A

0.83 V

Coating Type

Yellow/White Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

11.2 cm

1.88 cm²

21 cm³

4.34 cm²

80.9 cm²

7.32 cm

Core Loss

Bpk

140 G

Frequenzy

100 kHz

Core Loss (nominal)

83 mW/cm³

Core Loss (maximum)

95 mW/cm³

where Bpk expressed in gauss, f expressed in hertz, and:

a=1.00E+09, b=1.10E+08, c=1.90E+06, d=1.90E-13

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

50 Oe

55.2%

47.4%

where H expressed in oersteds, and:

a=1.00E-02, b=9.70E-06, c=1.72, d=0.00

Wire Size

AWG

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

111

139

174

RDC(Ω)

2.6 m

5.3 m

10.7 m

21.8 m

43.3 m

87.3 m

173.0 m

344.8 m

683.9 m

1.4

2.7

Full Winding

Turns

130

202

312

483

747

1,157

1,790

RDC(Ω)

3.5 m

8.4 m

20.6 m

50.9 m

125.2 m

309.4 m

760.0 m

1.9

4.6

11.3

27.9

T184-36

MATERIAL 36 (Permeabilität 75)

-26- & 36 Material: Ein sehr populäres Material, es ist ein kostengünstiges Allzweckmaterial, das in einer Vielzahl von Stromumwandlungs- und Netzfilteranwendungen nützlich ist.

Ein wasserstoffreduziertes Eisenmaterial, das Material '41' sehr ähnelt, aber einen erweiterten Frequenzbereich bietet.

50/60Hz - bis 500 kHz für Leistungsan

Bevorzugte Anwendungsbereiche:
Licht-Dimmer-Drosseln 50/60 Hz,

EMI-Netz Drosseln

DC-Drosseln <50 kHz

Leistungsfaktor-Korrektur Drosseln <50 kHz.

Kern

Farbe

Außen

Innen

Höhe

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

Product Group

T184-36

Weiß/Gelb

46.74

24.13

18.03

µ 75

1690

±10%

DC—1 MHz

150

gramm

A_Lvalue (nominal)

169 nH/ N²

μi (reference)

µ 75

Density gm/cm³

7.0

Test Winding

N=100, #24 AWG

Frequency

10 kHz

Voltage on Agilent 4284A

0.83 V

Coating Type

White/Yellow Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

11.2 cm

1.88 cm²

21 cm³

4.34 cm²

80.9 cm²

7.32 cm

Core Loss

Bpk

140 G

Frequenzy

100 kHz

Core Loss (nominal)

83 mW/cm³

Core Loss (maximum)

95 mW/cm³

where Bpk expressed in gauss, f expressed in hertz, and:

a=1.00E+09, b=1.10E+08, c=1.90E+06, d=1.90E-13

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

50 Oe

55.2%

47.4%

where H expressed in oersteds, and:

a=1.00E-02, b=9.70E-06, c=1.72, d=0.00

Wire Size

AWG

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

111

139

174

RDC(Ω)

2.6 m

5.3 m

10.7 m

21.8 m

43.3 m

87.3 m

173.0 m

344.8 m

683.9 m

1.4

2.7

Full Winding

Turns

130

202

312

483

747

1,157

1,790

RDC(Ω)

3.5 m

8.4 m

20.6 m

50.9 m

125.2 m

309.4 m

760.0 m

1.9

4.6

11.3

27.9

T184-52

-52 Material: Dieses Material hat geringere Kernverluste bei hoher Frequenz und die gleiche Durchlässigkeit wie das -26 und -36 Material. Es ist beliebt für Hochfrequenz-Choke-Designs und in einer Vielzahl von Geometrien verfügbar.

‐52 Material: This material has lower core losses at high frequency and the same permeability as the ‐26 and -36 Material. It is popular for high frequency choke designs and available in a wide variety of geometries.

Material 52 (Permeabilität 75)

50/60 Hz- Differential mode EMI Line-Chokes

z.B.350 µ H -100 Umdrehungen=35,0nH/N²

IRON POWDER TOROIDAL CORES FOR POWER AND AC LINE FILTE

Preis- und Lieferzeit auf Anfrage

Kern

Farbe

Außen

Innen

Höhe

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

Product Group

T184-52

Grün/Blau

46.74

24.13

18.03

µ 75

1590

±10%

DC-1 MHz

150

gramm

A_Lvalue (nominal)

159 nH/ N²

μi (reference)

µ 75

Density gm/cm³

7.0

Test Winding

N=100, #24 AWG

Frequency

10 kHz

Voltage on Agilent 4284A

0.83 V

Coating Type

Green/Blue Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

11.2 cm

1.88 cm²

21 cm³

4.34 cm²

80.9 cm²

7.32 cm

Core Loss

Bpk

140 G

Frequenzy

100 kHz

Core Loss (nominal)

58 mW/cm³

Core Loss (maximum)

67 mW/cm³

where Bpk expressed in gauss, f expressed in hertz, and:

a=1.00E+09, b=1.10E+08, c=2.10E+06, d=6.90E-14

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

50 Oe

61.6%

53.4%

where H expressed in oersteds, and:

a=1.00E-02, b=9.70E-06, c=1.72, d=0.00

Wire Size

AWG

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

111

139

174

RDC(Ω)

2.6 m

5.3 m

10.7 m

21.8 m

43.3 m

87.3 m

173.0 m

344.8 m

683.9 m

1.4

2.7

Full Winding

Turns

130

202

312

483

747

1,157

1,790

RDC(Ω)

3.5 m

8.4 m

20.6 m

50.9 m

125.2 m

309.4 m

760.0 m

1.9

4.6

11.3

27.9

T200-1

T200-1 (Permeabilität 20)

Ein "C"-gepulvertes Carbonyleisenmaterial, das dem Material '13' sehr ähnelt, aber einen höheren Volumenwiderstand und eine größere Stabilität aufweist.

Kern

Farbe

Außen

Innen

Höhe

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

Product Group

T200-1

Blau

50.80

31.75

13.97

µ 20

250

±10%

0.5-5 MHz

100

gramm

A_Lvalue (nominal)

25 nH/ N²

µ_i (reference)

µ 20

Density gm/cm³

6.4

Test Winding

N=100, #20 AWG

Frequency

10 kHz

Voltage on Agilent 4284A

0.56 V

Coating Type

Blue/Clear Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

13.0 cm

1.27 cm²

16.4 cm³

7.60 cm²

88.4 cm²

6.53 cm

Core Loss

Bpk

140 G

Frequenzy

100 kHz

Core Loss (nominal)

31mW/cm³

Core Loss (maximum)

36 mW/cm³

where Bpk expressed in gauss, f expressed in hertz, and:

a=1.90E+09, b=2.00E+08, c=9.00E+05, d=4.30E-15

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

200 Oe

82.2%

78.0%

where H expressed in oersteds, and:

a=1.00E-02, b=1.14E-06, c=1.43, d=0.00

Wire Size

AWG

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

119

149

185

231

RDC(Ω)

3.2 m

6.4 m

12.9 m

25.9 m

51.6 m

103.9 m

206.5 m

411.4 m

819.3 m

1.6

3.2

Full Winding

Turns

148

228

353

547

847

1,311

2,029

3,140

RDC(Ω)

5.4 m

13.2 m

32.2 m

80.0 m

196.0 m

482.5 m

1.2 m

2.9

7.2

17.7

43.7

T200-2

MATERIAL 2 (Permeabilität 10)

Ein "E"-gepulvertes Carbonyleisenmaterial mit großem Volumenwiderstand und hoher Güte im Bereich von 1 MHz bei 30 MHz. Wird von allen Eisenpulvermaterialien am meisten verwendet.

-2 & -14 Materialien: Die geringe Permeabilität dieser Materialien führt zu einer niedrigeren AC-Flussdichte als andere Materialien ohne zusätzlichen Lückenverlust. Das -14 Material ist ähnlich -2 Material mit einer höheren Permeabilität.

-2, -4, -6 & -7 Materialien: Dies sind die beliebtesten Carbonyleisenmischungen. Sie bieten hohe Q-Werte bis zu 40 MHz und sind am beliebtesten für Amateurfunk und eine Vielzahl anderer Kommunikationsanwendungen. Sie sind auch nützlich für moderate Bandtransformatoren im Frequenzbereich von 200 bis 400 MHz

lität

Der Kern ist als KW-Balun bis 1000 Watt einsetzbar.

Kern

Farbe

Außen

Innen

Höhe

Perme-abilität

A_L (nH/100Wdgg.²)

A_L-Toleranz

Frequenz-bereich

Mass

(approximate)

Product Group

T200-2

Rot

50.80

31.75

13.97

µ 10

120

±5%

1-30 MHz

gramm

A_Lvalue (nominal)

12 nH/ N²

µ_i (reference)

µ 10

Density gm/cm³

5.0

Test Winding

N=40, #20 AWG

Frequency

1 MHz

Voltage on Agilent 4284A

1.0 V

Coating Type

Red/Clear Epoxy Paint

Voltage Breakdown (min.)

500 Vrms, 60Hz

Limit

0.1 mA, 5 s

Magnetic

Dimensions

L_e Eff. Mag. Path Length (cm)

A_e

Eff. Mag. Cross Section (cm²)

V_eff Eff. Core Volume (cm³)

WA - Min. Eff. Window Area

sa - Surface Area

mlt - mean length per turn

13.0 cm

1.27 cm²

16.4 cm³

7.60 cm²

88.4 cm²

6.53 cm

Core Loss & Q

Q Test Winding

140 G

Q Frequenzy

2 MHz

Q min on HP4342A

332

where Bpk expressed in gauss, f expressed in hertz, and:

a=4.00E+09, b=3.00E+08, c=2.70E+06, d=9.60E-16

DC Saturation

H_dc

Percent Initial Perm (nom.)

Percent Initial Perm (min.)

200 Oe

95.9%

94.8%

where H expressed in oersteds, and:

a=1.00E-02, b=1.83E-07, c=1.46, d=0.00

Wire Size

AWG

3.150

2.500

2000

1.600

1.250

1000

0.800

0.630

0.500

0.400

0.315

Single Layer

Turns

119

149

185

231

RDC(Ω)

3.2 m

6.4 m

12.9 m

25.9 m

51.6 m

103.9 m

206.5 m

411.4 m

819.3 m

1.6

3.2

Full Winding

Turns

148

228

353

547

847

1,311

2,029

3,140

RDC(Ω)

5.4 m

13.2 m

32.2 m

80.0 m

196.0 m

482.5 m

1.2 m

2.9

7.2

17.7

43.7

Wir freuen uns, dass Sie unseren Webshop für Ringkerne und HF -Spezialbauteile besuchen.

Shop im Aufbau !! - Amidon.de